Crack-arrest at a bimaterial interface

Crack-arrest at a bimaterial interface,10.1016/0020-7683(81)90077-9,International Journal of Solids and Structures,P THEOCARIS,J MILIOS

Crack-arrest at a bimaterial interface   (Citations: 13)
BibTex | RIS | RefWorks Download
Journal: International Journal of Solids and Structures - INT J SOLIDS STRUCT , vol. 17, no. 2, pp. 217-230, 1981
Cumulative Annual
View Publication
The following links allow you to view full publications. These links are maintained by other sources not affiliated with Microsoft Academic Search.
    • ...The ability of a bilayerstructuretoinitiatebrittlefracturehasalsobeen exploited for the purposes of research on rapid crack propagation (Ivankovic and Williams 1993), arrest (Theocaris and Milios 1981), or on interface effects in composite materials (Cudré-Mauroux et al. 1991)...
    • ...While embrittlement has been observedbymanyauthors,fewagreeonitsmechanism; it has been attributed to the restriction of crazing in the core (So and Broutman 1982), the high elastic energy storedintheskin[DjiauwandFesko(1976)andCudré-Maurouxetal.(1991)],thepoorviscoelasticproperties of the skin (Verpy et al. 1994), the elastic property discontinuity of the interface (Theocaris and Milios 1981) and the effect of high strain rate on the ...

    Marie-Aude Godartet al. Effect of skin fracture on failure of a bilayer polymer structure

    • ...The ability of a bilayer structure to initiate brittle fracture has also been exploited for the purposes of research on rapid crack propagation (Ivankovic (1991)), arrest (Theocaris and Milios (1981)), or the interface eects in composite materials (Cudre-Mauroux et al. (1991))...
    • ...While embrittlement had been observed by many authors, few agree on its mechanism; it has been attributed to the restriction of crazing in the core (So and Broutman (1982)), the high elastic energy stored in the skin (Djiauw and Fesko (1976) and Cudre-Mauroux et al. (1991)), the poor viscoelastic properties of the skin (Verpy et al. (1994)), the elastic property discontinuity of the interface (Theocaris and Milios (1981)) and the eect of ...

    Marie-Aude Godartet al. Eect of skin fracture on failure of a bilayer polymer structure

    • ...They have extended their study to the magnitude and the variation of the crack propagation velocities during fracture in duplex plates under dynamic loading (Theocaris and Milios, 1981)...

    G. A. Papadopoulos. Crack-tip Caustics at a bi-Material Interface

    • ...On the other hand, the study of interaction of a transverse propagating crack with abimaterial interface [13], [14] or with a longitudinal crack and a hole (with its center on the axis of crack propagation) [!5], resulted always in a process of momentary crack arrest...

    J. Milioset al. Dynamic interaction of a propagating crack with a hole boundary

    • ...It was also observed that the crack branched into multiple cracks in some cases [8]...
    • ...A similar delay was also observed in another study [8]...
    • ...It was also observed that the initiation of crack in the glass after the interface takes a certain amount of time even when the duplex specimen did not have any adhesive layer [8]...

    Weinong Chen. Experimental Investigation on Dynamic Crack Propagation Through Interf...